How to make a hot-finished seamless pipe ?
The production of hot-finished seamless pipes involves several key steps, from heating steel billets to forming and finishing the pipes. Below is a detailed step-by-step process:
---
1. Raw Material Preparation
- Steel Billets: Round solid steel billets (continuous cast or hot-rolled) are selected based on the desired pipe grade (e.g., carbon steel, alloy steel, stainless steel).
- Inspection: Billets are checked for surface defects (cracks, voids) and chemical composition.
---
2. Heating the Billet
- Furnace Heating: Billets are heated in a rotary hearth furnace or induction furnace to 1200–1300°C (2192–2372°F) to make them malleable for piercing.
- Temperature Control: Precise heating ensures uniformity to avoid cracks during forming.
---
3. Piercing (Hot Piercing Mill)
- Mandrel Mill or Rotary Piercer: The heated billet is fed into a piercing mill, where a piercing plug (mandrel) and rollers create a hollow shell (called a "hollow bloom" or "mother tube").
- Process: The billet is cross-rolled and stretched over the mandrel to form a thick-walled tube.
---
4. Elongation (Rolling Process)
- Mandrel Mill or Plug Mill: The hollow shell is elongated using a series of tapered rolls and a mandrel to reduce wall thickness and increase length.
- Stretch Reduction Mill (Optional): Some mills use additional rolling stands to further refine dimensions.
---
5. Sizing and Reeling
- Sizing Mill: The pipe passes through a series of stands with grooved rolls to achieve the final outer diameter (OD) with tight tolerances.
- Reeling (Optional): Improves roundness and surface finish by lightly rolling the pipe.
---
6. Cooling
- Cooling Bed: The hot pipe is transferred to a cooling bed and air-cooled or controlled cooled (for specific metallurgical properties).
---
7. Straightening & Cutting
- Straightening: The pipe passes through a rotary straightening machine to correct any bends or deformations.
- Cutting: Pipes are cut to specified lengths using a saw or torch.
---
8. Heat Treatment (If Required)
- Annealing/Normalizing/Quenching & Tempering: Applied for pipes requiring specific mechanical properties (e.g., high-pressure applications).
---
9. Finishing & Inspection
- Surface Treatment:
- Shot blasting removes scale.
- Phosphating/oiling prevents corrosion.
- Non-Destructive Testing (NDT):
- Ultrasonic Testing (UT) for internal defects.
- Eddy Current Testing (ECT) for surface cracks.
- Hydrostatic Testing for pressure resistance.
- Dimensional Checks: OD, wall thickness, length, and straightness are verified.
---
10. Final Processing & Dispatch
- End Facing/Beveling (If Needed): For welding-ready pipes.
- Marking & Coating: Pipes are marked with grade, size, and manufacturer details.
- Packaging & Shipping: Pipes are bundled and shipped to customers.
---
Key Hot-Finished Seamless Pipe Mills
- Mandrel Mill Process (Most common for medium-sized pipes)
- Plug Mill Process (For thicker walls)
- Assel Mill (For precision pipes)
---
Advantages of Hot-Finished Seamless Pipes
- Superior strength & pressure resistance.
- Uniform microstructure (no welds).
- Suitable for high-temperature/pressure applications (oil & gas, power plants, boilers).